HSSE-V ( 3%V )
    Steels with good machinability
    Rm < 750 N/mm² (101,500 PSI)
    Nodular graphite, Malleable cast iron

    HSSE-V ( 3%V )
    Heat treated and heat-resistant steels
    Rm < 1,000 N/mm²
       ( <30 HRC / <290 HB / <145,000 PSI )

    HSSE-V ( 3%V )
    Stainless steels and structural steels
    Rm < 600 N/mm²
       ( <200 HB / <101,000 PSI )

    HSSE-H ( 8%Co )
    High alloyed steels
    Rm = 1,000 - 1,300 N/mm²
       ( 30 - 40 HRC / 300 - 385 HB /
        135,000 - 185,000 PSI )

    High alloyed steels
    hardness Rockwell = 40 - 63 HRC

    HSSE-V ( 3%V )
    Any Material, at least 12% Elongation
    COLD FORMING
    All ductile material

    HIGH-TECHNOLOGY
    Plain carbon steel, Stainless steel
    Alloyed / tempered steel up to tensile
       strength 1,300 N/mm²
    Spheroidal graphite, Malleable cast iron
    Long-chiping aluminium & Copper alloys

    HSSE-PS ( 3.1%V - 8.5%Co )
    Nickel alloys

    HSSE-PS ( 3.1%V - 8.5%Co )
    Titanium alloys

    HSSE-V ( 3%V )
    Grey cast iron

    HSSE-V ( 3%V )
    Wrought Aluminium alloys Si < 10%
       (long-chipping)

    HSSE-V ( 3%V )
    Cast Aluminium alloys Si < 10%
       (short-chipping)

    HSSE-V ( 3%V )
    Short chip brass, Bronze

    HSS Steels with good machinability
    Rm < 750 N/mm² (101,500 PSI)
    Nodular graphite, Malleable cast iron
    Long chip brass, Cast aluminium alloys
       Si > 10% ( short-chipping )

    HSSE ( 3%V )
    Heat treated and heat-resistant steels
    Rm < 1,000 N/mm²
       ( <30 HRC / <290 HB / <145,000 PSI )

    HSSE ( 3%V )
    Stainless steels and structural steels
    Rm < 600 N/mm²
       ( <30 HRC / <290 HB / <145,000 PSI )

    HSSE ( 3%V )
    High alloyed steels
    Rm = 1,000 - 1,300 N/mm²
       ( 30 - 40 HRC / 300 - 385 HB /
        135,000 - 185,000 PSI )

    Nut taps HSSE-V ( 3%V )
    Steels with good machinability
    Rm < 750 N/mm² (101,500 PSI)
    Nodular graphite, Malleable cast iron